Scotch-Weld 3MA 96416

Scotch-Weld 7000046373 2-Part Part Structural Adhesive, 50 mL Container Duo-Pak Syringe Container, Part A: Black/Part B: Milky White, 48 hr at 72 deg F Curing

Invoice description: Adhesive Scotch-weld 50m L Urethane Dp620ns Blk

UPC: 021200964169

UNSPSC: 31201600

Manufacturer PN: 7000046373

^$27.42 EA

Factory Order
Estimated to ship in 9 days

enlarge

Product Overview

Scotch-Weld, 7000046373, Structural Adhesive, 2-Part Part, Duo-Pak Syringe Container, 50 mL Container, Urethane Base, Composition: Part A: 4, 4-Diphenylmethane Diisocyanate, Poly Diphenylmethane-4,4-diisocyanate), Diphenylmethanediisocyanate Prepolymer, Silane Ester Derivative, Carbon Black/Part B: Polyether Polyol, Propoxylated Trimethylolpropane, Amorphous Silica, 1-4-cyclohexanedimethanol, Aluminum Oxide, Calcium Oxide, Isophorone Diamine, Potassium Oxide, Sodium Oxide, m-xylene-.alpha.alpha.-diamine, 20 min Work Life, 4 hr Functional Cure, 48 hr at 72 deg F Curing, Part A: Black/Part B: Milky White, 60 to 80 deg F, 1:1 Mixing Ratio, Part B: 32 g/L VOC, For Use On: Plastic, Metal, Glass, Ceramic, Wood, Hardboard and Rubber

Features
Non-sagging after dispensing so adhesive stays where placed
Low temperature flexibility and low shrinkage
Long open time provides ample opportunity to position and adjust work

Specifications

ApplicationConstruction, General Industrial and MRO

Base TypeUrethane

ColorPart A: Black/Part B: Milky White

CompositionPart A: 4, 4-Diphenylmethane Diisocyanate, Poly Diphenylmethane-4,4-diisocyanate), Diphenylmethanediisocyanate Prepolymer, Silane Ester Derivative, Carbon Black/Part B: Polyether Polyol, Propoxylated Trimethylolpropane, Amorphous Silica, 1-4-cyclohexanedimethanol, Aluminum Oxide, Calcium Oxide, Isophorone Diamine, Potassium Oxide, Sodium Oxide, m-xylene-.alpha.alpha.-diamine

Container Size50 mL

Container TypeDuo-Pak Syringe

Curing Time48 hr at 72 deg F

For Use OnPlastic, Metal, Glass, Ceramic, Wood, Hardboard and Rubber

Functional Cure4 hr

Mixing Ratio1:1

Temperature Range60 to 80 deg F

Type2-Part Part

VOC ContentPart B: 32 g/L

Work Life20 min